優(yōu)質(zhì)螺栓鋁合金犧牲陽極廠家

 優(yōu)質(zhì)螺栓鋁合金犧牲陽極廠家High quality bolt aluminum alloy sacrifice anode factory

立博防腐具有一流的服務(wù)一流的質(zhì)量是值得信賴的生產(chǎn)廠家Libo has a first-class service first-class quality is a trustworthy manufacturer

公司的主要產(chǎn)品有：
☆鎂合金犧牲陽極系列：鎂錳合金犧牲陽極，鐲式鎂合金犧牲陽極，鎂合金半連續(xù)鑄棒材、鎂合金板材
☆鋁合金犧牲陽極系列：普通鋁合金犧牲陽極，高效鋁合金犧牲陽極，高活化鋁合金犧牲陽極鐲式鋁合金犧牲陽極
☆鋅合金犧牲陽極系列：船用鋅合金犧牲陽極
☆配套產(chǎn)品：參比電極，測試樁，填包料，長效參比電極，便攜式參比電極，普通測試樁水泥測試樁
☆外加電流陰極保護(hù)：高硅鑄鐵陽極，深井陽極，

犧牲陽極、鎂合金犧牲陽極、鋁合金犧牲陽極、鋅合金犧牲陽極、鎂帶、鋅帶、參比電極、測試樁、鎂合金棒、鋅接地電池、第二代防雨防盜測試樁、絕緣接頭、以及陰極保護(hù)輔助材料，長效參比電極和外加電流用的高硅鑄鐵陽極、恒電位儀等產(chǎn)品。

鋁合金密度低，但強(qiáng)度比較高，接近或超過優(yōu)質(zhì)鋼，塑性好，可加工成各種型材，具有優(yōu)良的導(dǎo)電性、導(dǎo)熱性和抗蝕性，工業(yè)上廣泛使用，使用量僅次于鋼。一些鋁合金可以采用熱處理獲得良好的機(jī)械性能、物理性能和抗腐蝕性能。硬鋁合金屬AI—Cu—Mg系，一般含有少量的Mn，可熱處理強(qiáng)化．其特點(diǎn)是硬度大，但塑性較差。超硬鋁屬Al一Cu—Mg—Zn系，可熱處理強(qiáng)化，是室溫下強(qiáng)度的鋁合金，但耐腐蝕性差，高溫軟化快。鍛鋁合金主要是Al—Zn—Mg—Si系合金，雖然加入元素種類多，但是含量少，因而具有優(yōu)良的熱塑性，適宜鍛造，故又稱鍛造鋁合金。lb17184466

1) When the concentration of sulfuric acid(H2SO4) solution is high, the resulting membrane is easily colored, and the color is darker, and the membrane has a large porosity; When the concentration of sulfuric acid(H2SO4) solution is low, the color on the membrane is slow, and the color is lighter. The porosity of the membrane is relatively small. Therefore, a strong adsorption force and a flexible membrane can be used with a higher concentration of oxidation solution. If you want a hard and wear-resistant oxide film, you can use a lower concentration of oxidation liquid.
2) During anodic oxidation, the initial current density has a great influence on the structure of the oxide film. Excessive current density will cause the edge film of the sample to appear charred, and it will also cause the oxide film to be very rough. Therefore, during the anodic oxidation process, the current density should be gradually increased to a certain value, In the subsequent oxidation process, voltage fluctuations are also best not to exceed 2V. When the current density exceeds 3.3 A ? dm-2, the corrosion resistance of the oxide film decreases as the current density increases, but the current density does not exceed 3.3 A ? When dm-2, With the increase of current density, the gap rate of oxide film also increased, easy to dye, corrosion resistance is also better.lb17184466
3) Within 1 H, the growth of the oxide film is proportional to the oxidation time. However, when the oxidation time is too long, because the surface of the oxide film is dissolved by the electrolyte, the aperture of the oxide film gradually becomes larger and the film layer becomes rough.
鎂的電極電位為-2.375V
鋁的電極電位為-1.706V
鋅的電極電位為-0.763V
鐵的電極電位為-0.409V
銅的電極電位為+0.340V
鋅鋁合金的話就只能以較高的-0.763V考慮,那么如果以鋅鋁合金為犧牲陽極,那么可以用來保護(hù)鐵和銅等金屬,但不能保護(hù)鎂.
現(xiàn)階段主要有鎂鋁鋅三種陽極。鎂合金再用

土壤中、鋅合金用在海水中、鋁合金用在淡水中。
首先,陰極保護(hù)技術(shù)是電化學(xué)保護(hù)技術(shù)的一種,其主要原理是向被腐蝕金屬結(jié)構(gòu)物表面施加一個外加電流,使得被保護(hù)結(jié)構(gòu)物成為陰極,繼而讓金屬腐蝕發(fā)生的電子遷移得到抑制,避免或減弱了腐蝕的發(fā)生.
其次,就目前陰極保護(hù)技術(shù)而言,其實(shí)相對已經(jīng)發(fā)展成熟,而且廣泛應(yīng)用到土壤、海水、淡水、化工介質(zhì)中的鋼質(zhì)管道、電纜、鋼碼頭、艦船、儲罐罐底、冷卻器等金屬構(gòu)筑物等的腐蝕控制.
而且,陰極保護(hù)技術(shù)有兩種：犧牲陽極陰極保護(hù)和強(qiáng)制電流（外加電流）陰極保護(hù).焦作市立博輕合金股份有限公司是專業(yè)犧牲陽極、鎂合金犧牲陽極、鋁合金犧牲陽極、鋅合金犧牲陽極、