性能項(xiàng)目
|
試驗(yàn)條件[狀態(tài)]
|
測(cè)試方法
|
測(cè)試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
物理性能
|
|
---
|
|
|
|
|
吸濕率(平衡)
|
(23 C/50%RH)1L
|
ISO 15512
|
0.2
|
%
|
|
含濕量（最大）
|
23℃
|
ISO 62
|
0.6
|
%
|
|
粘度
|
MV,260 C,1500 1/sec
|
DIN 54811
|
311000
|
cP
|
|
模塑收縮量
|
Flow
|
ASTM D 955
|
0.005-0.007
|
cm/cm
|
|
熔體流動(dòng)速率
|
cm3/10min,melt volume rate,MVR at 260C/5.0 kg
|
ISO 1133
|
16
|
g/10min
|
|
機(jī)械性能
|
|
---
|
|
|
|
|
抗拉強(qiáng)度
|
Ultimate
|
|
Yield
|
|
Ultimate
|
|
Yield
|
|
|
5 mm/min
|
|
50 mm/min
|
|
5 mm/min
|
|
50 mm/min
|
|
|
ISO 527
|
|
ISO 527
|
|
ISO 527
|
|
ISO 527
|
|
|
|
|
|
|
50 mm/min
|
|
5 mm/min
|
|
5 mm/min
|
|
50 mm/min
|
|
|
ISO 527
|
|
ISO 527
|
|
ISO 527
|
|
ISO 527
|
|
|
|
|
拉伸模量
|
1mm/min
|
ISO 527
|
2.6
|
GPa
|
|
撓曲模量
|
2mm/min
|
ISO 178
|
2.5
|
GPa
|
|
屈服撓曲強(qiáng)度
|
2mm/min
|
ISO 178
|
85
|
MPa
|
|
IZOD沖擊值
|
缺口
|
|
無缺口
|
|
無缺口低溫
|
|
缺口低溫
|
|
|
80*10*4+23C
|
|
80*10*4+23C
|
|
80*10*4-30C
|
|
80*10*4-30C
|
|
|
ISO 178/1A
|
|
ISO 178/1U
|
|
ISO 178/1U
|
|
ISO 178/1A
|
|
|
|
|
|
|
at-30C,V-notch Edgew 80*10*4 sp=62
|
|
23C,V-notch Edgew 80*10*4 sp=62
|
|
|
|
|
|
泰伯磨耗值
|
CS-17,1kg
|
GE Test
|
62
|
---
|
|
電氣性能
|
體積電阻率
|
---
|
IEC 60093
|
Min 1e+015
|
Ohm-cm
|
|
表面電阻率
|
ROA
|
IEC 60093
|
Min 1e+015
|
Ohm
|
|
|
---
|
|
|
---
|
|
介電強(qiáng)度
|
in oil,3.2mm
|
|
in oil,1.6mm
|
|
in oil,0.8mm
|
|
---
|
|
IEC 60243-1
|
|
IEC 60243-1
|
|
IEC 60243-1
|
|
|
|
|
|
---
|
|
|
---
|
|
電弧電阻
|
Tungsten
|
ASTM D 495
|
5
|
sec
|
|
比較性漏電指數(shù)
|
---
|
IEC 60112/3rd
|
250
|
V
|
|
熱 性 能
|
導(dǎo)熱率
|
---
|
ISO 8302
|
0.2
|
W/m-K
|
|
熱畸變溫度
|
at 0.46MPa(66psi)
|
|
at 1.8MPa(264psi)
|
|
|
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm
|
|
HDT/Ae,1.82MPa Edgew 120*10*4 sp=100mm
|
|
|
|
|
|
|
---
|
|
|
|
|
UL熱指數(shù)
|
電性能
|
|
機(jī)械沖擊性能
|
|
非機(jī)械沖擊性能
|
|
---
|
|
|
|
|
|
---
|
|
|
---
|
|
可燃性測(cè)試
|
mm,IEC Needle Flame Test,10s,passes at
|
IEC 60695-2-2
|
1.6
|
---
|
|
含氧指數(shù)
|
---
|
ISO 4589
|
32
|
%
|
|
灼熱絲試驗(yàn)
|
passes at 1mm
|
IEC 60695-2-1
|
960
|
℃
|
|
其它性能
|
球體壓力測(cè)試
|
125C+/-2C
|
IEC 60035-1
|
passes
|
---
|