5CrNiMo|Φ6 軋材 低耐熱性模具鋼
5CrNiMo|Φ8 軋材 低耐熱性模具鋼
5CrNiMo|Φ10 軋材 低耐熱性模具鋼
5CrNiMo|Φ11 軋材 低耐熱性模具鋼
5CrNiMo|Φ12 軋材 低耐熱性模具鋼
5CrNiMo|Φ13 軋材 低耐熱性模具鋼
5CrNiMo|Φ14 軋材 低耐熱性模具鋼
5CrNiMo|Φ15 軋材 低耐熱性模具鋼
5CrNiMo|Φ16 軋材 低耐熱性模具鋼
5CrNiMo|Φ17 軋材 低耐熱性模具鋼
5CrNiMo|Φ18 軋材 低耐熱性模具鋼
5CrNiMo|Φ19 軋材 低耐熱性模具鋼
5CrNiMo|Φ20 軋材 低耐熱性模具鋼
5CrNiMo|Φ21 軋材 低耐熱性模具鋼
5CrNiMo|Φ22 軋材 低耐熱性模具鋼
5CrNiMo|Φ23 軋材 低耐熱性模具鋼
5CrNiMo|Φ24 軋材 低耐熱性模具鋼
5CrNiMo|Φ25 軋材 低耐熱性模具鋼
5CrNiMo|Φ26 軋材 低耐熱性模具鋼
5CrNiMo|Φ28 軋材 低耐熱性模具鋼
5CrNiMo|Φ29 軋材 低耐熱性模具鋼
5CrNiMo|Φ30 軋材 低耐熱性模具鋼
5CrNiMo|Φ32 軋材 低耐熱性模具鋼
5CrNiMo|Φ35 軋材 低耐熱性模具鋼
5CrNiMo|Φ38 軋材 低耐熱性模具鋼
5CrNiMo|Φ40 軋材 低耐熱性模具鋼
5CrNiMo|Φ42 軋材 低耐熱性模具鋼
5CrNiMo|Φ45 軋材 低耐熱性模具鋼
5CrNiMo|Φ48 軋材 低耐熱性模具鋼
5CrNiMo|Φ50 軋材 低耐熱性模具鋼
5CrNiMo|Φ130 鍛材 低耐熱性模具鋼
5CrNiMo|Φ140 鍛材 低耐熱性模具鋼
5CrNiMo|Φ145 鍛材 低耐熱性模具鋼
5CrNiMo|Φ150 鍛材 低耐熱性模具鋼
5CrNiMo|Φ155 鍛材 低耐熱性模具鋼
5CrNiMo|Φ160 鍛材 低耐熱性模具鋼
5CrNiMo|Φ165 鍛材 低耐熱性模具鋼
5CrNiMo|Φ170 鍛材 低耐熱性模具鋼
5CrNiMo|Φ175 鍛材 低耐熱性模具鋼
5CrNiMo|Φ180 鍛材 低耐熱性模具鋼
5CrNiMo|Φ185 鍛材 低耐熱性模具鋼
5CrNiMo|Φ190 鍛材 低耐熱性模具鋼
5CrNiMo|Φ195 鍛材 低耐熱性模具鋼
5CrNiMo|Φ200 鍛材 低耐熱性模具鋼
---------------------------------
材料名稱：合金工具鋼 牌號：5CrNiMo
標準：GB/T 1299-1985
●特性及適用范圍：
5CrNiMo鋼具有良好的韌性、強度和高耐磨性。它在室溫和500～600℃時的力學(xué)性能幾乎相同。在加熱到500℃時，仍能保持住HB300左右的硬度。由于鋼中含有鉬，因而對回火脆性并不敏感。從600℃緩慢冷卻下來以后，沖擊韌性僅稍有降低。
5CrNiMo鋼具有良好的淬透性。300mm×400mm×300mm的大塊鋼料，自820℃油淬和560℃回火后，斷面各部分的硬度幾乎一致。
該種鋼用來制造各種大、中型鍛模。易形成白點，需要嚴格控制冶煉工藝及鍛軋后的冷卻制度。
●化學(xué)成份：
碳 C ：0.50～0.60
硅 Si：≤0.40
錳 Mn：0.50～0.80
硫 S ：≤0.030
磷 P ：≤0.030
鉻 Cr：0.50～0.80
鎳 Ni：1.40～1.80
銅 Cu：允許殘余含量≤0.30
釩 V ：允許殘余含量＜0.2
鉬 Mo：0.15～0.30
●力學(xué)性能：
硬度 ：退火,241～197HB,壓痕直徑3.9～4.3mm
●熱處理規(guī)范及金相組織：
熱處理規(guī)范：淬火,830～860℃油冷。
●交貨狀態(tài)：鋼材以退火狀態(tài)交貨。
●物理性能/熱加工/預(yù)先熱處理/淬火/回火（詳細資料來電咨詢！！！）