| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.01> | % | |
| 線性模壓收縮率 | KPIC Method | 1.4-1.8 | % | ||
| 熔體流動速率 | ASTM D-1238 | 10 | g/10min | ||
| 密度 | ASTM D-1505 | 0.91 | g/cm3 | ||
| 機械性能 | 彎曲模量 | ASTM D-790 | 18,000 | ||
| 抗張強度(屈服) | ASTM D-638 | 330 | |||
| 斷裂伸長率 | ASTM D-638 | 200< | % | ||
| Izod沖擊強度(缺口) | ASTM D-256 | 10 | |||
| 介電強度 | Short Time | ASTM D-149 | 40 | KV/M | |
| 洛氏硬度 | ASTM D-785 | 102 | R Scale | ||
| 電氣性能 | 介電常數 | 1KHz | ASTM D-150 | 2.3 | |
| 耗散(損耗)因數 | 1KHz | ASTM D-150 | 2 | ||
| 耐電弧性 | ASTM D-495 | 130 | sec. | ||
| 體積電阻率 | ASTM D-257 | 1 | 1017ohm.H | ||
| 熱性能 | 熱膨脹系數(線性) | ASTM D-696 | 10 | 10-5H/H℃ | |
| 維卡軟化點 | ASTM D-1525 | 153 | ℃ | ||
| 熱傳導性 | KPIC Method | 3 | |||
| 熱變形溫度 | ASTM D-648 | 135 | ℃ | ||
| 比熱 | KPIC Method | 0.46 | ℃ | ||