| PA66 71G33L 美國杜邦公司 物性數(shù)據(jù) |
②原料技術(shù)數(shù)據(jù)
| 性能項目 |
試驗條件[狀態(tài)] |
測試方法 |
測試數(shù)據(jù) |
數(shù)據(jù)單位 |
| 基本性能 |
吸水率 |
24小時浸漬(23℃) |
ASTM D-570 |
0.5 |
% |
| 吸水率 |
飽和(23℃) |
ASTM D-570 |
4.6 |
% |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.35 |
--- |
| 機械性能 |
洛氏硬度M |
DAM |
ASTM D-785 |
M96 |
--- |
| 洛氏硬度M |
50%RH |
ASTM D-785 |
M90 |
--- |
| 洛氏硬度R |
DAM |
ASTM D-785 |
R122 |
--- |
| 洛氏硬度R |
50%RH |
ASTM D-785 |
R118 |
--- |
| 泰伯磨耗量 |
50%RH |
--- |
36 |
cycles |
| 拉伸強度 |
23℃,DAM |
ASTM D-638 |
151.6 |
MPa |
| 拉伸強度 |
23℃,50%RH |
ASTM D-638 |
110.3 |
MPa |
| 斷裂伸長率 |
23℃,DAM |
ASTM D-638 |
3 |
% |
| 斷裂伸長率 |
23℃,50%RH |
ASTM D-638 |
4 |
% |
| 擠剪強度 |
23℃,DAM |
ASTM D-732 |
72 |
MPa |
| 撓曲模量 |
23℃,DAM |
ASTM D-790 |
6895 |
MPa |
| 撓曲模量 |
23℃,50%RH |
ASTM D-790 |
5516 |
MPa |
| 撓曲強度 |
23℃,DAM |
ASTM D-790 |
228 |
MPa |
| 埃佐沖擊強度 |
23℃,DAM |
ASTM D-256 |
128 |
j/m |
| 埃佐沖擊強度 |
23℃,50%RH |
ASTM D-256 |
128 |
j/m |
| 電氣性能 |
介電強度 |
DAM |
ASTM D-149 |
630 |
volts/mil |
| 介電強度 |
100%RH |
ASTM D-149 |
255 |
volts/mil |
| 體積電阻率 |
100%RH |
ASTM D-257 |
109 |
ohm-cm |
| 損耗因數(shù) |
DAM@106Hz赫 |
ASTM D-150 |
0.02 |
--- |
| 體積電阻率 |
DAM |
ASTM D-257 |
1014 |
ohm-cm |
| 介電強度 |
(分步法)DAM |
ASTM D-149 |
510 |
volts/mil |
| 介電常數(shù) |
DAM@103Hz赫 |
ASTM D-150 |
4.2 |
--- |
| 介電常數(shù) |
DAM@106Hz赫 |
ASTM D-150 |
3.4 |
--- |
| 損耗因數(shù) |
DAM@103Hz赫 |
ASTM D-150 |
0.02 |
--- |
| 熱 性 能 |
熔點 |
50%RH |
ASTM D-789 |
255 |
℃ |
| 線性熱膨脹系數(shù) |
--- |
ASTM D-696 |
1.8×10-5 |
m/m/℃ |
| 熔點 |
DAM |
ASTM D-789 |
255 |
℃ |
| 熱畸變溫度 |
1.8MPa |
ASTM D-648 |
246 |
℃ |
| |
|