HB-YD114(Q)

1.6

50-55

(受強烈沖擊后

After high impact)

高錳鋼堆焊焊絲，受強烈沖擊后，表面具有加工硬度的特點。

High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.

HB-YD115(Q)

1.6

50-55

(受強烈沖擊后After high impact)

用于受嚴重沖擊高錳鋼堆焊，加工硬化效果顯著。

Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.

HB-YD165(Q)

1.6

60-65

高硬度耐磨焊絲，適用于磨粒磨損表面堆焊

High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.

HB-YD172(Q)

1.6

≥40

用于堆焊齒輪、挖泥斗、礦山機械等磨損件

Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.

HB-YD207(Q)

1.6

≥50

用于堆焊推土機 ，螺旋槳等磨損零件

Applied to repair surface of high wear parts, such as bulldozer blade and propeller.

HB-YD212(Q)

1.2/1.6

≥50

用于堆焊各種受磨損的機件表面，如齒輪、挖斗、礦山機械

Applied to repair surface of wear parts, such as gear mud bucket and mining machinery.

HB-YD256(Q)

1.6

HB≥170

高錳鋼堆焊，適用于破碎機等受沖擊磨損部位的堆焊

High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher.

HB-YD258(Q)

1.6

55-60

用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-YD265(Q)

1.6

60-65

高硬度耐磨焊絲，適用于磨粒磨損表面堆焊

High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.

HB-YD322(Q)

1.6

≥55

用于堆焊各種沖模及切削刃具，兼用于修復要求耐磨損性能較高之機械零件

Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.

HB-YD327A(Q)

1.6

≥55

專門用于模具堆焊，耐磨性能高于D322

Used tomouldsurfacing, wear resistance is better than D322.

HB-YD337(Q)

1.6

≥48

用于鑄鋼或鍛鋼上堆焊鍛模

Applied to repairforging dieatcast steelorforging steel.

HB-YD397(Q)

1.6

≥40

用于堆焊鑄鋼或鍛鋼做坯體的熱鍛模或堆焊高強度耐磨件

Applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing.

HB-YD405A(Q)

1.6

50-59

用于熱軋輥開坯輥堆焊

Applied to repair hot-rolling blooming rollor.

HB-YD430A(Q)

1.6

20-35

打底層堆焊焊絲

A backing hardfacing flux-cored Wires

HB-YD488A(Q)

1.6

45-50

用于軋輥堆焊

Applied to repair rollor

HB-YD507Mo(Q)

1.6

35-45

用于510℃以下中高壓閥門堆焊

Applied to valve which operating tdivperature is less than 510℃.

HB-YD518(Q)

1.6

40-50

用于連鑄輥堆焊

Applied to repaircontinuous caster roller

HB-YD688(Q)

1.6

50-60

用于磨煤輥打底焊(韌性好，可以多層堆焊)

Used to coal roller backing welding.

HB-YD788(Q)

1.6

55-62

硬度高，可以多層堆焊。

High hardness andmulti-layer welding

HB-YD888(Q)

1.2, 1.6

60-65

硬度高，堆焊層厚度不超過6mm。

High hardness, but thethicknessofsurfacing layeris less than 6mm.

HB-YD888Ni(Q)

1.2

58-65

高鉻合金焊絲，用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-YD988(Q)

1.6

55-63

高鉻合金焊絲，用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-YD990(Q)

1.6

55-65

用于高溫耐磨堆焊。

Applied to repair surface ofhigh tdivperaturewear parts.

HB-YD58(Q)

1.6

55-60

高溫耐磨焊絲，用于化推焦機磨靴的堆焊。

high tdivperaturewear hardfacing wires,

HB-YD67(Q)

1.6

58-63

用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-YD95(Q)

1.6

55-63

高鉻合金焊絲，用于耐磨表面堆焊

Applied to repair surface of wear parts.

HB-DG7(Q)

1.6

52-60

地鐵盾構施工 刃口堆焊專用，也可用于煤碳石裝載機料斗和刃口堆焊修復。

Applied to repair surface of high impact wear parts, such as shiled machine, exc ator bucket and hopper of mining machinery products.