Grade :
|
X55CrMo14耐腐蝕鋼、棒材
|
|
|
|
|
|
|
|
Number:
|
1.4110
|
|
|
|
|
|
|
|
Classification:
|
Martensitic stainless steel
|
|
|
|
|
|
|
|
Density:
|
7.7 g/cm 3
|
|
|
|
|
|
|
|
Standard:
|
|
|
|
|
|
|
|
|
EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件
|
|
|
|
|
|
|
|
EN 10088-1:2005不銹鋼。不銹鋼清單
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Equivalent grades:
|
No information
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition % of steel X55CrMo14 (1.4110): EN 10088-2-2005
|
|
|
|
|
|
|
|
|
Tighter carbon ranges may be agreed at the time of enquery and order
|
|
|
|
|
|
|
|
|
Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended.
|
|
|
|
|
|
|
|
|
Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
V
|
|
0.48 - 0.6
|
max 1
|
max 1
|
max 0.04
|
max 0.015
|
13 - 15
|
0.5 - 0.8
|
max 0.15
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X55CrMo14 (1.4110)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
850-950
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
12
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+A)
|
280
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|