4.0mm進(jìn)口MWA特種鋼焊條Mac Trode E630標(biāo)準(zhǔn)E307-17

英國進(jìn)口MWA鎳鉻錳特種鋼焊條Mac Trode E630|E307-17|錘鍛模修復(fù)|錳鋼堆焊

Tough high strength, fully austenitic electrode, designed to resist heat and impact. Fully machinable. Weld deposit will work harden under impact and retain properties at high temperatures. Easy to use in all positions producing sound welds, good build-up characteristics and good slag detachability. For joining or overlaying mild and alloy steels, spring steels, heat resisting steels, ideal for the repair of drop forging dies. Suitable for use as a buffer layer prior to hardsurfacing of manganese steel, and may be used for welding manganese steel rails or similar applications involving friction, impact or corrosion.

可靠的高強(qiáng)度全奧氏體焊條，設(shè)計用于耐熱和耐沖擊。完全可加工。焊縫熔敷層在沖擊下加工硬化，并在高溫下保持性能。易于全位置焊接并產(chǎn)生良好的焊縫，堆積特性和脫渣性俱佳。適用于連接或堆焊低碳鋼/合金鋼、彈簧鋼、耐熱鋼等，是修復(fù)錘鍛模的理想材料。適用于錳鋼堆焊前作緩沖層，也可用于焊接錳鋼鋼軌或涉及摩擦、沖擊或腐蝕的類似應(yīng)用。

Resists Heat & Impact. 耐熱和抗沖擊。

Very Ductile. 非常有韌性。

Ideal for Cracked Die Bottoms. 適用于開裂的模具底部。

Fully Work Hardenable. 完全加工硬化。

Retains Properties at High Temperatures. 在高溫下保持性能。

As Deposited 20HRC. 熔覆層硬度20HRC。

Work Hardened 35HRC. 加工硬化35HRC。

Typical All Weld Metal Chemical Analysis (%)

典型全焊縫金屬成分(%)

Typical All Weld Metal Mechanical Properties（As Welded）

典型全焊縫金屬機(jī)械性能（焊態(tài)）：

Ultimate Tensile Strength抗拉強(qiáng)度： 650 N/mm²

Elongation延伸率： 40%

Hardness硬度： 220 HB

Hardness (Work Hardened)硬度（工作硬化）： 350 HB

Sizes Available and Recommended Amperages

尺寸Φ/電流：

Current電流：AC/DC (+)

Related Specification參考標(biāo)準(zhǔn)：AWS A5.4 E307-17 | Type 20.10.4 Mn

Storage儲存：Electrodes should be stored in dry conditions. Should the electrodes  become damp, re-dry for one hour at 150°C before use. 焊條應(yīng)儲存在干燥環(huán)境中。如果焊條受潮，應(yīng)在250°C下重新干燥1小時后再使用。