Grade :
|
1.4113鐵素體耐腐蝕鋼片/板和帶材
|
|
|
|
|
|
|
Number:
|
X6CrMo17-1
|
|
|
|
|
|
|
Classification:
|
鐵素體不銹鋼
|
|
|
|
|
|
|
Density:
|
7.7 g/cm 3
|
|
|
|
|
|
|
Standard:
|
|
|
|
|
|
|
|
EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件
|
|
|
|
|
|
|
EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件
|
|
|
|
|
|
|
EN 10263-5:2001冷鐓和冷擠壓用鋼條、棒材和線材。不銹鋼交貨技術(shù)條件
|
|
|
|
|
|
|
EN 10088-1:2005不銹鋼。不銹鋼清單
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Equivalent grades:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical composition % of steel X6CrMo17-1 (1.4113): EN 10088-2-2005
|
|
|
|
|
|
|
|
未經(jīng)買方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對鑄件進(jìn)行精加工。
|
|
|
|
|
|
|
|
特定的硫含量范圍可以改善特定的財產(chǎn)。對于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對于可極化性，建議將硫含量控制在最大0.015%。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
|
max 0.08
|
max 1
|
max 1
|
max 0.04
|
max 0.015
|
16 - 18
|
0.9 - 1.4
|
|
|
|
|
|
|
|
|
|
Mechanical properties of steel X6CrMo17-1 (1.4113)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (+A)
|
440-660
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (+A)
|
280
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (+A)
|
18
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Nominal diameter (mm):
|
2月25日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Z - Reduction in cross section on fracture (%)
|
57-60
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HB): (+A)
|
200
|
|
|
|
|
|