牌號
|
SUS310S耐熱鋼棒和線材
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
其他名稱
|
SUS310S-HR
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
對應標準
|
JIS G 4311-2019
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
耐熱鋼棒和線材
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Heat-resisting steel bars and wire rods
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類
|
奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
耐腐蝕
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
說明
|
①本標準適用于耐熱鋼棒(圓鋼、角鋼、六角鋼及扁鋼的統稱,稱為棒材)及耐熱鋼線材(稱為線材)。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
②牌號后綴“-B”(熱軋棒材);后綴“-CB”(冷軋棒材)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
例如:熱軋棒材SUH1-B,SUS304-HR-B
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
冷軋棒材SUH1-CB,SUS304-HR-CB
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
③牌號后綴“-WR”表示線材。例如:SUH1-WR,SUS304-HR-WR
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
密度
|
7.98 g/cm3
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SUS310S 化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
|
|
|
|
|
|
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
24
|
19
|
|
|
|
|
|
|
|
|
最DA值
|
0.08
|
1.5
|
2
|
0.045
|
0.03
|
26
|
22
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SUS310S 機械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態
|
抗拉強度
|
屈服點
|
延伸率
|
斷面收縮率
|
硬度
|
|
|
|
|
|
|
|
|
|
σb
|
σs
|
δ
|
ψ
|
HBW
|
|
|
|
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
%
|
|
|
|
|
|
|
|
|
|
|
棒材;d≤180
|
固溶處理(S)
|
≥520
|
≥205
|
≥40
|
≥50
|
≤187
|
|
|
|
|
|
|
|
|
|
熱處理條件:固溶處理 溫度1030~1180°C,快冷
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1 近似對照表 奧氏體不銹鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
中國
|
中國臺灣
|
日本
|
韓國
|
美國
|
國際標準組織
|
德國
|
法國
|
歐標
|
俄羅斯
|
瑞典
|
英國
|
GB
|
ISC
|
CNS
|
JIS
|
KS
|
ASTM
|
UNS
|
ISO
|
DIN EN/DIN
|
W-Nr.
|
NF EN/NF
|
EN
|
數字牌號
|
GOST
|
SS
|
BS EN/BS
|
06Cr25Ni20
|
S31008
|
310S
|
SUS 310S
|
STS 310S
|
310S
|
S31008
|
~X12CrNi 23-13
|
X12CrNi 25-21
|
1.4845
|
Z12CN 25-20
|
X12CrNi 23-12
|
1.4845
|
10Х23Н18
|
2361
|
304S24
|
(0Cr25Ni20)
|
X6CrNi25-20
|
X6CrNi25-20
|
1.4951
|