Hostaform® LX90Z XAP2 ?
聚甲醛（POM）共聚物
Celanese Corporation
產品說明:
Preliminary Data Sheet
Hostaform® acetal copolymer grade LX90Z XAP2 ? is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform® LX90Z XAP2 ? has lower volatile emissions as required for some automotive interiors.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application.
Low Emission Performance [VDA-275] <5 PPM
|
供貨地區 |
|
|||||
|
添加劑 |
紫外線穩定劑 |
|||||
|
特性 |
低揮發 |
|||||
|
用途 |
|
|||||
|
RoHS 合規性 |
聯系制造商 |
|||||
|
外觀 |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
密度 |
1.43 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
8.00 |
cm3/10min |
ISO 1133 |
|||
|
收縮率 |
|
|
ISO 294-4 |
|||
|
橫向流量 |
1.4 |
% |
|
|||
|
流量 |
2.3 |
% |
|
|||
|
吸水率 (飽和, 23°C) |
0.75 |
% |
ISO 62 |
|||
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
2700 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應力 (屈服) |
54.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應變 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
|
彎曲模量 (23°C) |
2900 |
MPa |
ISO 178 |
|
|
|
|
|
機電之家網 - 機電行業權威網絡宣傳媒體
Copyright 2011 jdzj.com All Rights Reserved技術支持：杭州濱興科技有限公司
銷售熱線：0571-28292387 
在線客服：0571-87774297
展會合作/友情連接：0571-87774298
網站服務咨詢：0571-28292385
投訴熱線：0571-87774297
網站經營許可證:浙B2-20080178-4