⒌為保證焊接質量，對工件焊口應清理干凈，不準有油污、鐵銹、水分、油漆及污物等，對使用低氫型焊條尤為重要。
⒍對低氫型焊條，焊前焊條須經350℃烘焙1h，并隨烘隨用，否則易產生氣孔、夾渣、裂紋等缺陷。纖維素焊條一般不需烘焙，若受潮，按說明書規定溫度焊前烘焙，但溫度過高將破壞焊條的焊接工藝性能。
⒎說明書中規定的焊接電流為參考值，實際操作中應具體掌握，如工件預熱，可比正常電流低5%～15%；立焊和仰焊比平焊的電流小10%～15%；采用直流時可比交流減小10%左右。在使用直流焊機時，注意說明書規定焊接所階級性，否則影響焊接工藝。不銹鋼焊條
OK 61.20
(AWS A5.4)E308L-16
OK 61.25
(AWS A5.4)E308H-15
OK 61.30
(AWS A5.4) E308L-17
OK 61.35
(AWS A5.4)E308L-15
OK 61.50
(AWS A5.4) E308H-17

OK 61.80
(AWS A5.4)E347-17
OK 61.86
(AWS A5.4)E347-17
OK 62.53
(無對應)
OK 62.73
(無對應)
OK 62.75
(無對應)

OK 63.20
(AWS A5.4)E316L-16
OK 63.30
(AWS A5.4) E316L-17
OK 63.35
(AWS A5.4)E316L-15
OK 63.41
(AWS A5.4)E316L-26
OK 63.80
(AWS A5.4)E318-17

OK 64.30
(AWS A5.4)E317L-17
OK 64.63
(無對應)
OK 67.13
(AWS A5.4)E310-16
OK 67.15
(AWS A5.4)E310-15
OK 67.20
(AWS A5.4)E309MoL-16

OK 67.43
(AWS A5.4)E307-16
OK 67.45
(AWS A5.4)E307-15
OK 67.50
(AWS A5.4)E2209-17
OK 67.51
(AWS A5.4)E2209-26
OK 67.53
(AWS A5.4)E2209-16

OK 67.55
(AWS A5.4)E2209-15
OK 67.56
(無對應)
OK 67.60
(AWS A5.4)E309L-17
OK 67.62
(AWS A5.4) E309-26
OK 67.70
(AWS A5.4)E309LMo-17

OK 67.71
(AWS A5.4) E309LMo-26
OK 67.75
(AWS A5.4)E309L-15
OK 68.15
(AWS A5.4)E410-15
OK 68.17
(AWS A5.4)E410NiMo-16
OK 68.25
(AWS A5.4)E410NiMo-15

OK 68.37
(無對應)
OK 68.53
(AWS A5.4) E2594-16
OK 68.55
(AWS A5.4)E2594-15
OK 68.81
(AWS A5.4)E312-17
OK 68.82
(AWS A5.4)E312-17

OK 69.25
(AWS A5.4)E316LMn-15
OK 69.33
(AWS A5.4)E385-16
OK 61.81
(AWS A5.4)E347-16
OK 61.85
(AWS A5.4)E347-15
OK 63.34
(AWS A5.4) E316L-16

不銹鋼實芯焊絲
OK AUTROD 16.95
(AWS A5.9)ER307mod
OK AUTROD 308LSi
(AWS A5.9)ER308LSi
OK AUTROD 309L
(AWS A5.9)ER309L
OK AUTROD 309LSi
(AWS A5.9)ER309LSi
OK AUTROD 310
(AWS A5.9) ER310

OK AUTROD 316LSi
(AWS A5.9)ER316LSi
OK AUTROD 318Si
      (無對應)
OK AUTROD 347Si
(AWS A5.9)ER347Si
OK AUTROD 385
(AWS A5.9)ER385
OK AUTROD 430LNb
      (無對應)

OK AUTROD 430Ti
      (無對應)
OK AUTROD 2209
(AWS A5.9)ER2209
OK AUTROD 2307
    (無對應)
OK AUTROD 2509
(AWS A5.9)ER2594

鋁焊絲
 OK TIGROD 1070 
      (無對應)
 OK TIGROD 1100
(AWS A5.10)R1100
 OK TIGROD 5087
(AWS A5.10)R5087
 OK TIGROD 5554
(AWS A5.10)R5554
OK TIGROD 5556A
(AWS A5.10)R5556

   TIGROD 1450
      (無對應)
  TIGROD 4043
(AWS A5.10)R4043
  TIGROD 4047
(AWS A5.10)R4047
  TIGROD 5183
(AWS A5.10)R5183
 TIGROD 5754
     (無對應)

不銹鋼藥芯焊絲
OK TUBROD 14.27
(AWS A5.22)E2209T1-1
OK TUBROD 14.28
(AWS A5.22)E2553T1-G
OK TUBROD 14.37
(AWS A5.22)E2209T0-1
SHIELD-BRIGHT 308L X-tra
(AWS A5.22)E308LT0-1
SHIELD-BRIGHT 309L X-tra
(AWS A5.22)E309LT0-1

SHIELD-BRIGHT 309L
(AWS A5.22)E309LT1-1
SHIELD-BRIGHT 316L X-tra
(AWS A5.22)E316LT0-1
SHIELD-BRIGHT 316L
(AWS A5.22)E316LT1-1
SHIELD-BRIGHT 308L
(AWS A5.22)E308LT1-1

低碳鋼藥芯焊絲
OK E71T-1
(AWS A5.36)E71T1-C1A0-CS2-H4
FILARC PZ6111HS
(AWS A5.36)E70T1-C1A0-G-H8
FILARC PZ6113S
(AWS A5.36)E71T1-C1A2-CS2
FILARC PZ6130HS
(AWS A5.36)E70T-5CJ H4
FILARC PZ6111
(AWS A5.36)E70T1-C1A0-G

FILARC PZ6113
(AWS A5.36)E71T1-C1A0-CS2-H4
OK TUBROD 14.18
(AWS A5.36)E70T-4
OK TUBROD 15.00
(AWS A5.36)E71T5-M21A2-CS1-H4
OK TUBROD 15.00S
(AWS A5.17)F7A4-EC1
OK TUBROD 15.02
(AWS A5.20)E71T-5M

OK TUBROD 15.10
(AWS A5.20)E70T-1C
OK TUBROD 15.12
(AWS A5.20)E70T-1C
OK TUBROD 15.14
(AWS A5.20)E71T1-C1A0-CS2-H8
OK TUBROD 15.15
(AWS A5.20)E71T1-C1A0-CS2
OK TUBROD 15.16
(AWS A5.20)E70T-1C

OK TUBROD 15.18
(AWS A5.20)E70T-1C
VERTOMAX 2MG
(AWS A5.20)EG70T-Ni1

低碳鋼焊絲
 COREWELD 46 LS
(AWS A5.36)E71T15-M20A4-CS1 H4
   COREWELD 89
(AWS A5.36)E120T15-M20A4-G-H4
 FILARC PZ6102
(AWS A5.36)E71T15-M21A4-CS1-H4
 FILARC PZ6104
(AWS A5.36)E71T15-M21A6-G-H4
 FILARC PZ6105R
(AWS A5.36)E70T15-M12A4-G-H4

 FILARC PZ6159
      (無對應)
OK TUBROD 14.00S
(AWS A5.17) F7A2-EC1
OK TUBROD 14.07S
    (無對應)
OK TUBROD 14.11
(AWS A5.36)E70T15-M12A4-G-H4
 OK TUBROD 14.12
(AWS A5.36)E71T15-C1A2-CS1

OK TUBROD 14.13
(AWS A5.36)E71T15-M21A2-CS1


品名 類別 AWS型號 熔敷金屬化學成分 熔敷金屬力學性能 特性及用途
C Mn Si P S Cr Ni Cu Mo 屈服點Mpa 抗拉強度Mpa 伸長率(%) 面績縮減率(%)
低合金鋼藥芯焊絲 Dual Shield 8100W E81T1-W2 0.04 1.01 0.59 0.015 0.011 0.54 0.58 0.56 550 620 26 61 特別開發的熔敷符合低合金、高強度耐候鋼顏色配套的需要，在U.S.S.Cor-Ten專業測試中顯示，在大氣中曝露后，無法識別焊接熔敷與母材顏色間的不同
Dual Shield 7000-A1 E81T1-A1 0.05 1.02 0.57 0.51 540 610 26 63 75%Ar/25%CO2混合氣能改善電弧特性，增加潤濕性，減少熔涌及容易電弧控制，金屬過渡平順，焊縫無氣孔