分類:
|
E9018-G, SFA/AWS A5.5, E 55 6 Mn1NiMo B T 32 H5, EN ISO 18275-A
|
|
認證:
|
E9018-G, ABS, 3.2 - 4.0 mm, NAKS/HAKC, UNA 272581, Seproz
|
Approvals are based on factory location. Please contact ESAB for more information.
|
Alloy Type:
|
C, Mn, 1% Ni
|
|
Coating Type:
|
Basic
|
|
Diffusible Hydrogen:
|
<5.0 ml/100g
|
|
Welding Current:
|
AC, DC+-
|
焊縫金屬分析
夏比V型缺口沖擊性能
|
Impact Value
|
Testing Temperature
|
|
ISO PWHT 580°C 1h
|
|
80 J
|
-50 °C
|
|
60 J
|
-60 °C
|
Typical Tensile Properties
|
Elongation
|
Tensile Strength
|
Yield Strength
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
|
ISO PWHT 580°C 1h
|
|
21 %
|
710 MPa
|
650 MPa
|
-
|
-
|
|
AWS Stress relieved
|
|
-
|
-
|
-
|
620 °C
|
1 hr
|
熔敷數據
|
Fusion time per electrode at 90% I max
|
kg weld metal/kg electrodes
|
Number of electrodes/kg weld metal
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
|
60 hr
|
0.60 kg
|
83.3
|
55-85 A
|
0.72 kg/h
|
24.4 V
|
2.5 x 350 mm
|
|
68 hr
|
0.55 kg
|
56.6
|
80-140 A
|
0.94 kg/h
|
23.3 V
|
3.2 x 350 mm
|
|
103 hr
|
0.60 kg
|
24.4
|
120-180 A
|
1.43 kg/h
|
24.0 V
|
4.0 x 450 mm
|